SINGLE PACK QUICK DRYING HIGH GLOSS ENAMEL QF61
qf61-fastrac-20

A single pack quick drying high gloss and high build finish coating, based on modified alkyd resin.

  • Suitable as a one coat finish or as part of a fast drying protective system for steel.
  • Touch dry in 20 minutes.
  • Excellent protective properties against corrosion.
  • Conforms to BS 5493 Part FF3A/B.

SUITABLE FOR:

Degreased, suitably prepared new metal, previous suitable coatings, clean and abraded as necessary.

APPLICATION:
Brush, Roller & Spray

SHEEN LEVEL:
High Gloss

COVERAGE:
10mper Litre

TOUCH DRY:
20 mins

RECOAT:
4 Hrs Min.

AVAILABILITY:
5 Litre

POT LIFE:
N/A

ADDITIONAL INFO:
Thinner: TX31

Primer: AP71

*At 50 microns DFT (loss factors will apply in practice)

BS, ACE and RAL

Correct preparation is vital to ensure you obtain the full benefit from Bradite Metal Paints.

New and unpainted steel

  • High pressure water cleaning to remove all loose salts and other contaminants.
  • Degrease using BRADITE TD39, with scrubbing plus high pressure water cleaning to remove any oil contamination not removed by high pressure cleaning alone, rinse with clean water and allow to dry.
  • Mechanically or manually prepared steel to a clean metallic finish, SIS-St 3 minimum.
  • Substrate to be dry, clean and free of contamination and dust free prior to coating.

Existing coatings

  • Jet wash to remove all loose and flaking paint, salts and other contaminants.
  • Degrease using Bradite TD39 diluted with up to 9 parts of warm water and scrubbing to remove any oil contamination not removed with jet washing alone. Rinse with clean water and allow to dry.
  • Existing coatings should be well adhered with all edges tight and well feathered.
  • Bare or rusted steel should be manually or mechanically abraded to a clean metallic finish (SIS-St 3).
  • Substrate should be clean, dust free and dry before application.
  • Spot prime with correct primer.
  • Galvanised steel, aluminium and other non-ferrous metals should be roughened or lightly abraded.
  • New bright galvanised steel should be degreased and treated with Bradite TM38 pre-treatment for galvanised steel.
ALTERNATIVE PRODUCTS

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy

CLADIT

CLADDING FINISH WC44
just5lcladit-copy